Changing in irradiation behavior and temperature-coefficient variation caused by light-induced degradation of a-Si/μc-Si solar cells
J.A. Weicht, F. Hamelmann, G. Behrens, in: 2015 IEEE 42nd Photovoltaic Specialist Conference (PVSC), IEEE, 2015, pp. 1–4.
Download
Es wurde kein Volltext hochgeladen. Nur Publikationsnachweis!
Konferenzbeitrag
| Veröffentlicht
| Englisch
Autor*in
Abstract
In our work we observe the light behavior before and after light-induced degradation of amorphous/microcrystalline (a-Si/μc-Si) tandem silicon-based solar cells. We show that during light-induced degradation the efficiency increases for illumination levels lower than standard test condition illumination. Additionally we examine the temperature coefficient of the open circuit voltage, short circuit current and fill factor. The temperature-coefficient of silicon-based thin film solar cells varies during the light-induced degradation.
Erscheinungsjahr
Titel des Konferenzbandes
2015 IEEE 42nd Photovoltaic Specialist Conference (PVSC)
Seite
1-4
Konferenz
2015 IEEE 42nd Photovoltaic Specialists Conference (PVSC)
Konferenzort
New Orleans, LA
FH-PUB-ID
Zitieren
Weicht, Johannes A. ; Hamelmann, Frank ; Behrens, Grit: Changing in irradiation behavior and temperature-coefficient variation caused by light-induced degradation of a-Si/μc-Si solar cells. In: 2015 IEEE 42nd Photovoltaic Specialist Conference (PVSC) : IEEE, 2015, S. 1–4
Weicht JA, Hamelmann F, Behrens G. Changing in irradiation behavior and temperature-coefficient variation caused by light-induced degradation of a-Si/μc-Si solar cells. In: 2015 IEEE 42nd Photovoltaic Specialist Conference (PVSC). IEEE; 2015:1-4. doi:10.1109/PVSC.2015.7356298
Weicht, J. A., Hamelmann, F., & Behrens, G. (2015). Changing in irradiation behavior and temperature-coefficient variation caused by light-induced degradation of a-Si/μc-Si solar cells. In 2015 IEEE 42nd Photovoltaic Specialist Conference (PVSC) (pp. 1–4). New Orleans, LA: IEEE. https://doi.org/10.1109/PVSC.2015.7356298
@inproceedings{Weicht_Hamelmann_Behrens_2015, title={Changing in irradiation behavior and temperature-coefficient variation caused by light-induced degradation of a-Si/μc-Si solar cells}, DOI={10.1109/PVSC.2015.7356298}, booktitle={2015 IEEE 42nd Photovoltaic Specialist Conference (PVSC)}, publisher={IEEE}, author={Weicht, Johannes A. and Hamelmann, Frank and Behrens, Grit}, year={2015}, pages={1–4} }
Weicht, Johannes A., Frank Hamelmann, and Grit Behrens. “Changing in Irradiation Behavior and Temperature-Coefficient Variation Caused by Light-Induced Degradation of a-Si/Μc-Si Solar Cells.” In 2015 IEEE 42nd Photovoltaic Specialist Conference (PVSC), 1–4. IEEE, 2015. https://doi.org/10.1109/PVSC.2015.7356298.
J. A. Weicht, F. Hamelmann, and G. Behrens, “Changing in irradiation behavior and temperature-coefficient variation caused by light-induced degradation of a-Si/μc-Si solar cells,” in 2015 IEEE 42nd Photovoltaic Specialist Conference (PVSC), New Orleans, LA, 2015, pp. 1–4.
Weicht, Johannes A., et al. “Changing in Irradiation Behavior and Temperature-Coefficient Variation Caused by Light-Induced Degradation of a-Si/Μc-Si Solar Cells.” 2015 IEEE 42nd Photovoltaic Specialist Conference (PVSC), IEEE, 2015, pp. 1–4, doi:10.1109/PVSC.2015.7356298.
Google Scholar