Magneto-Optical Investigation of Surface Magnetization in Comparison with Bulk Magnetization

Exchange-biased specimens were produced by molecular beam epitaxy (MBE) of ferromagnetic (FM) Co-on-CoO substrates after the substrates had been irradiated by heavy ions to induce defects in the antiferromagnet (AFM). Measurements were obtained at different temperatures for different sample orientations with respect to the external magnetic field. While the EB was relatively small, measurements of the bulk magnetization at low temperatures revealed unusually shaped hysteresis loops. The surface magnetization, however, showed simple, nearly rectangular hysteresis loops. This study focuses on the advantage of complementary information on surface and bulk magnetization from optical and non-optical measurement methods.